PE Homopolymer LITEN MB 71
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Resistance to environmental stress cracking | ISO22088 | 5.00 hr | |
| Melt flow ratio- | 25.0 | ||
| density | ISO1183 | 0.963 g/cm³ | |
| melt mass-flow rate | ISO1133 | 8.0 g/10min | |
| ISO1133 | 25 g/10min | ||
| Shrinkage rate | ISO294-4 | 1.9 % | |
| ISO294-4 | 3.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 58 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2 | 1250 MPa | |
| Tensile stress | Yield | ISO527-2 | 25.0 MPa |
| Tensile strain | Yield | ISO527-2 | 8.5 % |
| Tensile creep modulus | ISO899-1 | 565 MPa | |
| ISO899-1 | 275 MPa | ||
| Flexural modulus | ISO178 | 1100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 5.5 kJ/m² | |
| ISO179 | 6.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO306 | 126 °C | |
| melting temperature | ISO11357-3 | 136 °C | |
| ISO75-2/A | 45.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.