Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.36 -- |
| Shrinkage rate | | % | 0.35到0.45 -- |
| Water absorption rate | | % | 0.80 -- |
| HeatStability | | °C | 130到135 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | kJ/m² | 11 17 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 9300 6800 |
| tensile strength | | MPa | 170 120 |
| elongation | | % | 3.0 4.5 |
| Flexural modulus | | MPa | 8000 5500 |
| bending strength | | MPa | 255 175 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | kV/mm | 22 -- |
| Volume resistivity | | ohms·cm | 1E+15 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | >200 -- |
| | °C | >240 -- |
| melting temperature | | °C | 250到260 -- |
| | cm/cm/°C | 2.5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.