Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 熔体质量流动速率 | | ASTMD1238 | 14to20 g/10min |
| 收缩率 | MD | ASTMD955 | 0.70 % |
| 吸水率 | 24hr | ASTMD570 | 0.37 % |
| 密度 | | ASTMD792 | 1.30 g/cm³ |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 0.45MPa,未退火 | ASTMD648 | 214 °C |
| 热变形温度 | 1.8MPa,未退火 | ASTMD648 | 207 °C |
| 玻璃转化温度 | | ASTME1356 | 220 °C |
| 线性热膨胀系数 | MD | ASTMD696 | 5.6E-05 cm/cm/°C |
| 导热系数 | | ASTMC177 | 0.35 W/m/K |
| 光学性能 | Test Condition | Test Method | Test Result |
|---|
| 折射率 | | ASTMD542 | 1.672 |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| FlameRating5 | 0.75mm,ALLcolors,ULfileE36098 | UL94 | V-0 |
| 极限氧指数 | | ASTMD2863 | 38 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | | ASTMD638 | 2340 Mpa |
| 抗张强度 | 屈服 | ASTMD638 | 69.6 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 69.6 Mpa |
| 伸长率 | 屈服 | ASTMD638 | 7.2 % |
| 伸长率 | 断裂 | ASTMD638 | 60 % |
| 弯曲模量 | | ASTMD790 | 2410 Mpa |
| 弯曲强度 | 屈服 | ASTMD790 | 91.0 Mpa |
| 压缩模量 | | ASTMD695 | 1730 Mpa |
| 压缩强度 | | ASTMD695 | 98.9 Mpa |
| 剪切强度 | | ASTMD732 | 62.7 Mpa |
| 泊松比 | | ASTME132 | 0.42 |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 体积电阻率 | | ASTMD257 | 9E+15 ohms·cm |
| 介电强度 | | ASTMD149 | 14 KV/mm |
| 介电常数 | 60Hz | ASTMD150 | 3.44 |
| 介电常数 | 1kHz | ASTMD150 | 3.40 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 悬壁梁缺口冲击强度 | | ASTMD256 | 690 J/m |
| 悬壁梁缺口冲击强度 | | ASTMD256 | NoBreak |
| 拉伸冲击强度 | | ASTMD1822 | 399 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.