Technical Data Sheet
| Biochemical properties | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | % | JIS K7105 |
| other | Test Condition | Test Method | Test Result |
|---|
| notes | | | 透明 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO R1133 | 2.8 g/10min |
| density | | ISO 1183 | 1080 Kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-1 | 55 MPa |
| fracture strain | | ISO 527-1 | 25 % |
| bending strength | | ISO 178 | 84 MPa |
| Flexural modulus | | ISO 178 | 2500 MPa |
| Tensile modulus | | ASTM D638/ISO 527 | 55(MPa) kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 2500(MPa) kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 84(MPa) kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.08 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2 | 72 ℃ |
| vicat | | ISO 306 | 85 ℃ |
| combustibility | | UL 94 | HB |
| Combustibility (rate) | | UL 94 | HB |
| vicat | | ASTM D1525/ISO R306 | 85 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.