PC/ABS CS9610 -111 SABIC INNOVATIVE NANSHA

Form：Granules

Properties:

High mobilityHigh impact resistance

Typical Applications:

Automotive interior partsElectrical applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Electrical applications
Properties:	High mobility \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	45	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	72.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.0mm	UL 94	V-0
NBSSmokeDensity	Flaming,Dmax	ASTME662	225
	NBSSmokeDensity	Flaming,Ds,1.5min	ASTME662	40.0
	NBSSmokeDensity	NBSSmokeDensity	Flaming,Ds,4min	ASTME662	150
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--3	ASTM D638	2600	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
bending strength	--6,7	ISO 178	98.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	98.0	Mpa
tensile strength	Yield4	ASTM D638	64.0	Mpa
	tensile strength	Yield	ISO 527-2/50	62.0	Mpa
		tensile strength	Break4	ASTM D638	62.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0	Mpa
elongation	Yield4	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	4.8	%
		elongation	Break4	ASTM D638	55	%
		elongation	elongation	Break	ISO 527-2/50	>45	%
Bending modulus	50.0mmSpan5	ASTM D790	2440	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	118	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	105	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	106	°C
Vicat softening temperature	--	ISO 306/B50	124	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	127	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260°C/5.0kg	ASTM D1238	15	g/10min
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	12.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.