PLA+PMMA

PLA+PMMA Plexiglas® Rnew® B522 Altuglas International of Arkema Inc.

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.480
transmissivity	3180μm	ASTM D1003	86.0 %
turbidity	3180μm	ASTM D1003	<5.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	43 J/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2340 MPa
tensile strength	Break	ASTM D638	49.6 MPa
Bending modulus		ASTM D790	2200 MPa
bending strength	Yield	ASTM D790	70.3 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ASTM D648	67.2 °C
Vicat softening temperature		ASTM D15253	76.1 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.19 g/cm³
melt mass-flow rate	230°C/3.8kg	ASTM D1238	3.9 g/10min
Shrinkage rate	MD	ASTM D955	0.20to0.60 %
Water absorption rate	24hr	ASTM D570	0.30 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	77

Supplementary Information	Test Condition	Test Method	Test Result
ASTMClassification		ASTM D788	PMMAUnspecified
RenewableCarbonConent		ASTM D6866	35 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.