PBT/PET ECOT3230 LANXESS GERMANY

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30℃-30°C	ISO 179/1eA	< 10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃23°C	ISO 179/1eA	< 10	kJ/m²
Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	65	kJ/m²
Impact strength of cantilever beam gap	-30℃-30°C	ISO 180-1A	< 10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃23°C	ISO 180-1A	< 10	kJ/m²
Suspended wall beam without notch impact strength	-30℃-30°C	ISO 180/1U	55	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23℃23°C	ISO 180/1U	55	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23℃23℃	ISO 527-1-2	10400	Mpa
tensile strength	Break，23℃Break，23℃	ISO 527-2/5	145	Mpa
Tensile strain	Break，23℃Break，23℃	ISO 527-2/5	2.8	%
Bending modulus	23℃23℃4	ISO 178-A	10300	Mpa
bending strength	23℃23℃4	ISO 178	230	Mpa
Bending strain			3	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	B120B120	ISO 306/B120	205	°C
Melting temperature		ISO 11357-3	225 to 250	°C
Linear coefficient of thermal expansion	TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.000090	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000030	1/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23°C	ISO 1183	1.55	g/cm³
Apparent density		ISO 60	0.8	g/cm³
Melt Volume Flow Rate (MVR)	260℃，5 kg260℃/5.0 kg	ISO 1133	30	cm3/10min
Shrinkage rate	TD：270℃，2.0 mmAcross Flow : 518°F, 0.0787 in 22	ISO 294-4	0.9	%
	Shrinkage rate	TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.2	%
		Shrinkage rate	MD：270℃，2.0 mmFlow : 518°F, 0.0787 in 22	ISO 294-4	0.3	%
		Shrinkage rate	Shrinkage rate	MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.1	%
Water absorption rate	Saturation，23℃Saturation，23℃	ISO 62	0.3	%
Water absorption rate	Water absorption rate	Equilibrium，23℃，50% RHEquilibrium，23℃，50% RH	ISO 62	0.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution ASolution A	IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.