PA66 FR350J NT0727 NA
29
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 294 | 1.7 % | ||
| Shrinkage rate flow 2.0mm 23 ℃ | ISO 294 | 1.4 % | |
| ISO 62 | 0.8 % | ||
| Water absorption rate 23 ° C50RH equilibrium | ISO 62 | 1.9 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus at 23 ℃ | ISO 527 | 3200 Mpa | |
| Tensile strength fracture at 23 ℃ | ISO 527 | 70 Mpa | |
| Elongation at 23 ℃ | ISO 527 | 15 % | |
| Poisson's ratio | ISO 527 | 0.4 | |
| ISO 178 | 90 Mpa | ||
| Bending modulus at 23 ℃ | ISO 178 | 3200 Mpa | |
| Cantilever beam notch impact at 23 ℃ | ISO 180 | 4.1 kJ/m² | |
| 23 ° C1eA type impact of simply supported beam gap | ISO 179 | 4.3 kJ/m² | |
| Simply supported beam without notch impact at 23 ℃ | ISO 179 | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistance 0.75mm | IEC 60093 | 1000000000000000000 Ω.㎝ | |
| Insulation strength 1.0mm | IEC 60243 | 17 KV/mm | |
| CTI 3.0mm | IEC 60112 | 250〜399 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Peak unannealed "MPa | ISO 75 | 75 °C | |
| Network melting temperature | ISO 11357 | 265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.