PPO(PPE)+PS+PP NORYL PPX™ PPX7200 resin

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	0.988 g/cm³
density	density		ISO 1183	0.990 g/cm³
melt mass-flow rate		ASTM D1238	16 g/10min
Melt volume flow rate		ISO 1133	18.0 cm³/10min
Shrinkage rate		内部方法	0.60to0.80 %
Shrinkage rate	Shrinkage rate		内部方法	0.60to0.80 %
Water absorption rate		ISO 62	0.050 %
Water absorption rate	Water absorption rate		ISO 62	0.020 %

Mechanical properties	Test Condition	Test Method	Test Result
Flexural modulus		ISO 178	1610 MPa
bending strength		ISO 178	48.0 MPa
bending strength	bending strength		ASTM D790	49.0 MPa
Tensile modulus		ISO 527-2/1	1670 MPa
tensile strength	Yield	ASTM D638	33.8 MPa
	tensile strength	Yield	ISO 527-2/50	34.0 MPa
		tensile strength	Break	ASTM D638	27.6 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	28.0 MPa
elongation	Yield	ASTM D638	10 %
Tensile strain	Yield	ISO 527-2/50	8.2 %
Tensile modulus		ASTM D638	1240 MPa
elongation	Break	ASTM D638	130 %
Tensile strain	Break	ISO 527-2/50	120 %
Flexural modulus		ASTM D790	1450 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	6.1 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap		ASTM D256	0.85 J/m
	Impact strength of cantilever beam gap		ASTM D256	150 J/m
		Impact strength of cantilever beam gap		ISO 180/1A	8.0 kJ/m²
			Impact strength of cantilever beam gap		ISO 180/1A	14 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D4812	1400 J/m
Suspended wall beam without notch impact strength		ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180/1U	NoBreak
Dart impact		ASTM D3763	36.2 J

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	110 °C
	Heat distortion temperature		ASTM D648	71.1 °C
	Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	73.4 °C
vicat		ASTM D152510	146 °C
	vicat		ISO 306/B50	103 °C
	vicat	vicat		ISO 306/B120	107 °C
Linear coefficient of thermal expansion		ASTME831	9.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion		ISO 11359-2	9.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion		ASTME831	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	1.1E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.