ABS TAIRILAC® AG15A1-H FCFC TAIWAN

898

Properties:
High gloss
Moderate impact
Universal level
Usages:
calculator
Clock housing
Phone
suitcase
Toy
Sound enclosure
Certificates:
TDS
Processing
MSDS
UL
RoHS
SVHC
Environmental
TDS
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	220°C/10.0kg	ASTMD1238	22	g/10min
Melt mass flow rate	Melt mass flow rate	200°C/5.0kg	ISO1133	2.2	g/10min
density		ASTMD792	1.04	g/cm³
density	density	23°C	ISO1183	1.04	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Impact strength of cantilever beam gap	23°C,4.00mm	ISO180	25	k/Jm2
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTMD256	220	J/m
tensile strength	23°C	ASTMD638	43	Mpa
tensile strength	tensile strength	屈服,23°C	ISO527-2	47.0	Mpa
Rockwell hardness	R计秤,23°C	ASTMD785	110
Rockwell hardness	Rockwell hardness	R计秤,23°C	ISO2039-2	110
Bending modulus	23°C	ISO178	2550	Mpa
Bending modulus	Bending modulus	23°C	ASTMD790	26000	kg/cm2
bending strength	23°C	ASTMD790	830	kg/cm2
bending strength	bending strength	23°C	ISO178	73	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
vicat softening point		ASTMD15253	93	°C
vicat softening point	vicat softening point		ISO306/A	93	°C
Hot deformation temperature	1.8MPa,Unannealed,6.35mm	ISO75-2/A	86.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,6.35mm	ASTMD648	92.0	°C

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	1.5mm,AllColors	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

ABS TAIRILAC® AG15A1-H FCFC TAIWAN

Technical Data Sheet