PP HCPO-CX02 82 00900
20
- Usages:For cars
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 15 g/10min | |
| density | ISO 1183 | 0.905 g/cm | |
| Shrinkage rate | SABIC method | 1.6 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Yield tensile strength | ISO 527 | 30 Mpa | |
| Tensile strength at break | ISO 527 | 24 Mpa | |
| elongation | ISO 527 | 600 % | |
| Flexural modulus | ASTM D-790 | 1700 Mpa | |
| IZOD notch impact strength | ISO 180/4A | 8.5 KJ/m | |
| ISO 180/4A | 6.0 KJ/m | ||
| ISO 180/4A | 4.5 KJ/m | ||
| Charpy notch impact strength | ISO 179/1eA | 7.0 KJ/m | |
| hardness | ISO 868 | 70 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D-696 | 120 µm/mK | ||
| ISO 75/B | 105 °C | ||
| vicat | ISO 306/A | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.