Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 6.0 % |
| Water absorption rate | | ISO 62 | 1.8 % |
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| density | | ISO 1183 | 1.35 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 9350 MPa |
| tensile strength | Break | ISO 527-2 | 160 MPa |
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 8500 MPa |
| bending strength | | ISO 178 | 235 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 85 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| relative permittivity | | IEC 60250 | 3.50 |
| relative permittivity | | IEC 60250 | 3.30 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
| Heat distortion temperature | | ISO 75-2/A | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare