Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.16 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | 250-270 °C |
| Temperature | | | 60-100 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.39 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 20 cm3/10min |
| Water absorption rate | | | 0.4 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus of elasticity | | ISO 527-1/-2 | 6900 Mpa |
| tensile strength | | ISO 527-1/-2 | 100 Mpa |
| elongation | | | 2.5 % |
| bending strength | | ISO 178 | 151 Mpa |
| Impact strength of simply supported beam without notch | | | 55 kJ/m² |
| Charpy Notched Impact Strength | | | 7 kJ/m² |
| ball indentation hardness | | ISO 2039-1 | 153 Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Glass Fiber Content | | | 20 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| combustibility | | UL94 | HB |
| | | 160 °C |
| | ISO 11359-1/-2 | 0.4 E-4/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.