Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 1.8 g/10 min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmittance | | ASTM D1003/ISO 13468 | 91.0 % |
| other | Test Condition | Test Method | Test Result |
|---|
| Color | | | 透明 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 5.0 % |
| tensile strength | | ASTM D638/ISO 527 | 70.3 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 95 |
| bending strength | | ASTM D790/ISO 178 | 108 kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 95 |
| tensile strength | | ASTM D638 | 70.3 Mpa |
| elongation | | ASTM D638 | 5.0 % |
| bending strength | | ASTM D790 | 108 Mpa |
| Impact strength of cantilever beam gap | | ASTM D256 | 20 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.16 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 1.8 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | < 1.0 % |
| Yellowness Index | | ASTM D1003 | 0.50 to 1.0 YI |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648/ISO 75 | 100 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 113 ℃（℉） |
| Heat distortion temperature | | ASTM D648 | 100 °C |
| vicat | | ASTM D1525 | 113 °C |
| UL flame retardant rating | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.