Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate - saturation | | ISO62 | 0.95 % |
| density | | ISO1183 | 1.30 g/cm³ |
| SpiralFlow | | 内部方法 | 16.0 cm |
| SpiralFlow | | 内部方法 | 19.0 cm |
| SpiralFlow | | 内部方法 | 68.0 cm |
| Shrinkage rate | | ISO294-4 | 1.6 % |
| Shrinkage rate | | ISO294-4 | 1.2 % |
| Shrinkage rate | | ISO294-4 | 1.4 % |
| Shrinkage rate | | ISO294-4 | 1.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 85 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO11443 | 225 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 4200 MPa |
| Tensile stress | | ISO527-2 | 115 MPa |
| Tensile strain | | ISO527-2 | 25 % |
| Flexural modulus | | ISO178 | 4000 MPa |
| Bending stress | | ISO178 | 190 MPa |
| Bending stress | | ISO178 | 130 MPa |
| Bending stress | | ISO178 | 110 MPa |
| Bending stress | | ISO178 | 35.0 MPa |
| compression stress | | ISO604 | 145 MPa |
| compression stress | | ISO604 | 90.0 MPa |
| compression stress | | ISO604 | 35.0 MPa |
| Bending stress | | ISO178 | 20.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 无断裂 |
| Impact strength of cantilever beam gap | | ISO180/A | 6.0 kJ/m² |
| | ISO180 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 150 V |
| dielectric constant | | IEC60250 | 3.00 |
| Dissipation Factor | | IEC60250 | 4E-03 |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 23 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/Af | 172 °C |
| Glass Transition Temperature | | ISO11357-2 | 162 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| | ISO11359-2 | 5.5E-05 cm/cm/°C |
| | ISO11359-2 | 1.3E-04 cm/cm/°C |
| thermal conductivity | | ISO22007-4 | 0.29 W/m/K |
| thermal conductivity | | ISO22007-4 | 0.32 W/m/K |
| Glass Transition Temperature | | ISO11357-2 | 169 °C |
| melting temperature | | ISO11357-3 | 387 °C |
| | ISO11359-2 | 4.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.