Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183/B | 1.20 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 37 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 60.0 MPa |
| tensile strength | Break | ISO 527-2 | 70.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 6.0 % |
| Tensile strain | Break | ISO 527-2 | 110 % |
| Flexural modulus | | ISO 178 | 2350 MPa |
| bending strength | | ISO 178 | 95.0 MPa |
| Tensile modulus | | ISO 527-2 | 2400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| needle flame test | | IEC 60695-11-5 | 通过 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 kV/mm |
| dielectric constant | | IEC 60250 | 2.70 |
| dielectric constant | | IEC 60250 | 2.70 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 141 °C |
| vicat | | ISO 306/B50 | 146 °C |
| Ball pressure temperature | | IEC 60335-1 | >125 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 144 °C |
| Heat distortion temperature | | ISO 75-2/A | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare