Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.040 % |
| Ash Content | | 内部方法 | 20 % |
| Water absorption rate | | ISO62 | 0.35 % |
| Shrinkage rate | | 内部方法 | 0.50 % |
| density | | ASTMD792 | 1.44 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 18 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 110 Mpa |
| Tensile modulus | | ASTMD638 | 6800 Mpa |
| bending strength | | ASTMD790 | 180 Mpa |
| elongation | | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 6400 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 70 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTMD150 | 3E-03 |
| Surface Resistivity | | ASTMD257 | 1E+14 ohms |
| dielectric strength | | ASTMD149 | 22 KV/mm |
| CTI | | IEC60112 | 350 V |
| dielectric constant | | ASTMD150 | 3.70 |
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 206 °C |
| vicat | | ASTMD15252 | 210 °C |
| | ASTMD696 | 3.5E-05 cm/cm/°C |
| | ASTMD648 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.