'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PET 545 NC010 DUPONT USA
185
Form：Granules | Grade：Enhanced level
Properties:
enhanceGlass fiber reinforcedHigh temperature resistanShort fiber reinforcement
Typical Applications:
Fiber grade
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Fiber grade |
| Properties: | enhance | Glass fiber reinforced | High temperature resistan | Short fiber reinforcement |
Certificates
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| characteristic | 45%矿物/玻纤增强.强度和刚度.尺寸稳定性和抗蠕变 | |||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 | kJ/m² |
| 23°C | ISO 179/1eU | 60 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | <100 | mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.75mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO 6452 | 0.0 | g |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ASTM D412/ISO 527 | 15500 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 100 | ||
| Bending modulus | ASTM D790/ISO 178 | 13500 | kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 15500 | Mpa | |
| tensile strength | Break | ISO 527-2 | 182 | Mpa |
| Tensile strain | Break | ISO 527-2 | 2.0 | % |
| Tensile creep modulus | 1hr | ISO 899-1 | 15600 | Mpa |
| 1000hr | ISO 899-1 | 13300 | Mpa | |
| Bending modulus | ISO 178 | 13500 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Combustibility (rate) | UL 94 | HB | ||
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 250 | ℃（℉） |
| HDT | ASTM D648/ISO 75 | 226 | ℃（℉） | |
| Effective thermal diffusivity coefficient | 1.4E-07 | m²/s | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 226 | °C |
| 8.0MPa,Unannealed | ISO 75-2/C | 180 | °C | |
| Vicat softening temperature | ISO 306/B50 | 230 | °C | |
| Melting temperature | ISO 11357-3 | 252 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 | cm/cm/°C |
| TD | ISO 11359-2 | 8.3E-05 | cm/cm/°C | |
| thermal conductivity | 0.32 | W/m/K | ||
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ASTM D792/ISO 1183 | 1690 | ||
| Shrinkage rate | ASTM D955 | 0.85 | % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.14 | % | |
| Top out temperature | 170 | °C | ||
| Melt Volume Flow Rate (MVR) | 280°C/2.16kg | ISO 1133 | 2.50 | cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.80 | % |
| MD | ISO 294-4 | 0.20 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 0.62 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.14 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257/IEC 60093 | 1.00E+14 | Ω | |
| Dielectric constant | ASTM D150/IEC 60250 | 4.5 | ||
| ASTM D150/IEC 60250 | 4.4 | |||
| Volume resistivity | ASTM D257/IEC 60093 | 1.00E+13 | Ω.cm | |
| Surface resistivity | IEC 60093 | 1E+14 | ohms | |
| Volume resistivity | IEC 60093 | 1E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 32 | KV/mm | |
| Relative permittivity | 100Hz | IEC 60250 | 4.50 | |
| 1MHz | IEC 60250 | 4.40 | ||
| Dissipation factor | 100Hz | IEC 60250 | 7E-03 | |
| 1MHz | IEC 60250 | 0.011 | ||
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 2 | |
| IEC 60112 | PLC 2 | |||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ISO 2039-2 | 100 | |
| R-Sale | ISO 2039-2 | 120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.