PA/MXD6 RENY™ 1021UCS MITSUBISHI ENGINEERING JAPAN
120
- Properties:High rigidityHigh impactFiller: Glass fiber reinf50% filler by weight
- Usages:Electronic and Electrical ApplicationsAutomotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 13 g/10min | |
| Melt volume flow rate | ISO 1133 | 11.1 cm3/10min | |
| Shrinkage rate | 0.40 % | ||
| Water absorption rate | ISO 62 | 0.47 % | |
| ISO 62 | 1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO 527-2 | 2.5 % | |
| Flexural modulus | ISO 178 | 18300 Mpa | |
| bending strength | ISO 178 | 392 Mpa | |
| Tensile modulus | ISO 527-2 | 17800 Mpa | |
| tensile strength | ISO 527-2 | 252 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 87 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 227 °C | |
| ISO 75-2/A | 217 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.