PP Copolymer CP-M 1815 R
0
- Usages:Application in the automotive field
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 0.900到0.940 g/cm³ | |
| melt mass-flow rate | ISO1133 | 16到20 g/10min | |
| Shrinkage rate | 1.3到1.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 60到65 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Break | ISO527-2 | >8.0 % |
| Tensile modulus | ISO527-2 | 1200到2000 MPa | |
| Tensile stress | Yield | ISO527-2 | >20.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | >15 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO306/B | 90.0 °C | |
| ISO3146 | 160 °C | ||
| ISO75-2/A | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.