PA66 LNP™ THERMOCOMP™ RF00AS-BK1A817
47
- Properties:High temperature resistan
- Usages:Electronic and Electrical ApplicationsChemical equipmentsporting goodsmechanical
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D 955 | 0.3 % | |
| ISO 294 | 0.34 % | ||
| ASTM D 955 | 1.2 % | ||
| Water absorption rate | ASTM D 570 | 0.4 % | |
| ISO 62 | 0.74 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM E831 | 27 E-6 °C | |
| ISO 11359-2 | 28.1 E-6 °C | ||
| ASTM E831 | 43.2 E-6 °C | ||
| ISO 11359-2 | 44.2 E-6 °C |
| combustibility | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | 1.5 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 197 Mpa | |
| ISO 527 | 194 Mpa | ||
| elongation at break | ASTM D638 | 2.4 % | |
| ISO 527 | 2.4 % | ||
| bending strength | ASTM D790 | 312 Mpa | |
| ISO 178 | 300 Mpa | ||
| Flexural modulus | ASTM D790 | 12540 Mpa | |
| ISO 178 | 14500 Mpa | ||
| Tensile modulus | ASTM D638 | 17650 Mpa | |
| ISO 527 | 14000 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 149 J/m | |
| ISO 180/1A | 13 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 65 kJ/m² | |
| ASTM D4812 | 1585 J/m | ||
| Instrumented dart impact energy peak at 23 ℃ (73 ℉) | ASTM D3763 | 12 J | |
| Multi axis impact | ISO 6603 | 3 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.