PA6 235N
0
- Properties:Performance characteristicsfast production stagewith core
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.13 g/cm3 | |
| Flow shrinkage rate | ASTM D955 | 0.80-1.1 % | |
| Water absorption rate | ASTM D570 | 1.6 % | |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| density | ASTMD792 | 1.13 g/cm³ | |
| Shrinkage rate | ASTMD955 | 0.80到1.1 % | |
| Water absorption rate | ASTMD570 | 1.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTMD256 | 48 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTMD638 | 82.7 MPa | |
| elongation | Break | ASTMD638 | 17 % |
| Flexural modulus | ASTMD790 | 3030 MPa | |
| bending strength | ASTMD790 | 117 MPa | |
| tensile strength | ASTM D638 | 82.7 MPa | |
| elongation | Break | ASTM D638 | 17 % |
| Flexural modulus | ASTM D790 | 3030 MPa | |
| bending strength | ASTM D790 | 117 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 48 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 185 °C | ||
| ASTMD648 | 71.1 °C | ||
| ASTM D648 | 71.1 ℃ | ||
| ASTM D648 | 185 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.