Epoxy Ebalta AH 100 / TG
0
CompareTechnical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Resin | 按重量计算的混合比:100 | ||
| Hardener | 按重量计算的混合比:20 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.64到0.66 Pa·s | |||
| Curing Time | 10到12 hr | ||
| STORAGE STABILITY | 40到50 min | ||
| density | 1.10到1.14 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO7619 | 79到85 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| compression stress | ISO604 | 75.0到85.0 MPa | |
| Flexural modulus | ISO178 | 2600到3000 MPa | |
| Bending stress | ISO178 | 95.0到105 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 20到40 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.