Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Mold shrinkage rate | | ASTM D-955 | 0.005-0.007 mm/mm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile breaking strength | | ASTM D-638 | 59 Mpa |
| Tensile impact strength | | ASTM D-1822 | 631 KJ/m |
| Rockwell hardness | | ASTM D-785 | 59 M Scale |
| tensile yield strength | | ASTM D-638 | 61 Mpa |
| Flexural modulus | | ASTM D-790 | 2330 Mpa |
| bending strength | | ASTM D-790 | 98 Mpa |
| elongation | | ASTM D-638 | 115 % |
| Impact Strength | | ASTM D-256 | 未破裂 |
| Tensile modulus | | ASTM D-638 | 2380 Mpa |
| Notch impact strength | | ASTM D-256 | 694 J/m |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Glow filament test | | IEC 695-2-1 | 960 °C |
| | ASTM D-2863 | 36 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Comparison of Arc Track Index | | IEC 112 | 225 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 151 °C |
| | ASTM D-648 | 137 °C |
| | ASTM D-696 | 65×10 mm/mm/℃ |
| | ASTM D-648 | 127 °C |
| Spherical indentation temperature | | IEC 598-1 | ＞125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.