PP GLS PP AN06 EH2 GLS Polymers Pvt. Ltd.

Usages:
Applications in furniture housing automotive electrical and electronic fields
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.20mm	ASTM D256	450to500 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	3.20mm	ASTM D256	450to500 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
UL flame retardant rating	UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	20.0to25.0 MPa
tensile strength		ASTM D638	22.0to28.0 MPa
elongation	Yield	ASTM D638	>20 %
Bending modulus		ASTM D790	1000to1500 MPa
bending strength		ASTM D790	20.0to25.0 MPa
tensile strength		ASTM D638	22.0to28.0 MPa
elongation	Yield	ASTM D638	>20 %
Bending modulus		ASTM D790	1000to1500 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	40.0to46.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	40.0to46.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	0.780to1.18 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	1.0to2.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	1.2to1.8 %
density		ASTM D792	0.780to1.18 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	1.0to2.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	1.2to1.8 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.