| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 62 | 2.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12500 Mpa |
| tensile strength | | ISO 527-2 | 200 Mpa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 12500 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 33 KV/mm |
| relative permittivity | | IEC 60250 | 4.80 |
| relative permittivity | | IEC 60250 | 4.40 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 290 °C |
| Heat distortion temperature | | ISO 75-2/A | 290 °C |
| melting temperature | | ISO 11357-3 | 295 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3.5E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4.0E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.