Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.20 % |
| ThermalConductivityofMelt | | | 0.14 W/m/K |
| density | | ISO1183 | 1.22 g/cm³ |
| melt mass-flow rate | | ISO1133 | 9.0 g/10min |
| Melt volume flow rate | | ISO1133 | 8.50 cm³/10min |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| Water absorption rate | | ISO62 | 0.60 % |
| MediumDensity | | | 1.04 g/cm³ |
| SpecificHeatCapacity of Melt | | | 2160 J/kg/°C |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 63 |
| | ISO868 | 58 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO3795 | <100 mm/min |
| FMVSS flammability | | FMVSS302 | B |
| Fogging-G-value | | ISO6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Odor | | VDA270 | 2.50 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 25 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 110 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | 19 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 81 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 260 MPa |
| Tensile stress | Yield | ISO527-2 | 19.0 MPa |
| Tensile stress | Break | ISO527-2 | 41.0 MPa |
| Tensile stress | | ISO527-2 | 12.0 MPa |
| Tensile stress | | ISO527-2 | 15.0 MPa |
| Tensile strain | Yield | ISO527-2 | 27 % |
| Tensile strain | Break | ISO527-2 | >300 % |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | Across Flow | ISO34-1 | 150 kN/m |
| tear strength | | ISO34-1 | 160 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 85.0 °C |
| Heat distortion temperature | | ISO75-2/A | 45.0 °C |
| brittle temperature | | ISO974 | -100 °C |
| vicat | | ISO306/A50 | 195 °C |
| vicat | | ISO306/B50 | 100 °C |
| melting temperature | | ISO11357-3 | 211 °C |
| EffectiveThermal Diffusivity | | | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.