Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183 | 1.19 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20-0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 105 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 89.0 % |
| transmissivity | | ASTM D1003 | 91.0 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D4218 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D4218 | NoBreak |
| Dart impact | | ASTM D3763 | 48.0 J |
| Dart impact | | ASTM D3763 | 45.0 J |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 55.0 J |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 71.0 J |
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 370 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 6.3 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 46.0 Mpa |
| tensile strength | | ISO 527-2 | 47.0 Mpa |
| tensile strength | | ASTM D638 | 53.0 Mpa |
| tensile strength | | ISO 527-2 | 49.0 Mpa |
| elongation | | ASTM D638 | 5.0 % |
| Tensile strain | | ISO 527-2 | 4.0 % |
| elongation | | ASTM D638 | 310 % |
| Tensile strain | | ISO 527-2 | 210 % |
| Flexural modulus | | ASTM D790 | 1900 Mpa |
| Flexural modulus | | ISO 178 | 1750 Mpa |
| bending strength | | ISO 178 | 64.0 Mpa |
| bending strength | | ASTM D790 | 67.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 73.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 73.0 °C |
| Heat distortion temperature | | ASTM D648 | 65.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 66.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.