Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| spiral flow length | | 内部方法 | 8.00 cm |
| Shrinkage rate | | ISO 294-4 | 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.10 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| MeltViscosity | | ISO 11443 | 525 Pa·s |
| density | | ISO 1183 | 1.41 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 88 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 6.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1U | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO 604 | 210 MPa |
| compression stress | | ISO 604 | 95.0 MPa |
| compression stress | | ISO 604 | 65.0 MPa |
| Tensile modulus | | ISO 527-2 | 28000 MPa |
| tensile strength | | ISO 527-2 | 275 MPa |
| tensile strength | | ISO 527-2 | 170 MPa |
| tensile strength | | ISO 527-2 | 110 MPa |
| tensile strength | | ISO 527-2 | 80.0 MPa |
| tensile strength | | ISO 527-2 | 70.0 MPa |
| Tensile strain | | ISO 527-2 | 1.7 % |
| Flexural modulus | | ISO 178 | 23500 MPa |
| bending strength | | ISO 178 | 400 MPa |
| bending strength | | ISO 178 | 265 MPa |
| bending strength | | ISO 178 | 185 MPa |
| bending strength | | ISO 178 | 100 MPa |
| compression stress | | ISO 604 | 300 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D4496 | 1E+05 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 368 °C |
| Glass Transition Temperature | | ISO 11357-2 | 152 °C |
| Glass Transition Temperature | | ISO 11357-2 | 160 °C |
| melting temperature | | ISO 11357-3 | 373 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 3.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
| thermal conductivity | | ISO 22007-4 | 0.95 W/m/K |
| thermal conductivity | | ISO 22007-4 | 2.1 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.