Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MediumDensity | | | 1.19 g/cm³ |
| density | | ISO1183 | 1.39 g/cm³ |
| melt mass-flow rate | | ISO1133 | 12 g/10min |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| Shrinkage rate | | ISO294-4 | 1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 3 | | ISO3795 | 55 mm/min |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Fogging-G-value | | ISO6452 | 2E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emissions of Organic Compounds | | VDA277 | 3.40 µgC/g |
| Emission | | VDA275 | <8.00 mg/kg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2300 Mpa |
| Tensile stress | | ISO527-2 | 54.0 Mpa |
| Tensile strain | | ISO527-2 | 17 % |
| Nominal tensile fracture strain | | ISO527-2 | 28 % |
| Flexural modulus | | ISO178 | 2000 Mpa |
| Bending stress | | ISO178 | 60.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 146 °C |
| Heat distortion temperature | | ISO75-2/A | 76.0 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare