PA66 A3WG10 BASF GERMANY
281
Form:Granules | Grade:Enhanced level
Properties:
Oil resistantDimensional stabilityHigh rigidityheat-resistingFiller: Glass fiber reinf50%Filler by weight
Typical Applications:
Industrial applications
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Industrial applications |
| Properties: | Oil resistant | Dimensional stability | High rigidity | heat-resisting | Filler: Glass fiber reinf | 50% | Filler by weight |
Certificates

Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179 | 13 | kJ/m² |
| 23°C | ISO 179 | 15 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 85 | kJ/m² |
| 23°C | ISO 179 | 95 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180 | 14 | kJ/m² |
| 23°C | ISO 180 | 17 | kJ/m² | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | 23°C | ISO 527-2 | 17000 | Mpa |
| tensile strength | Break,23°C | ISO 527-2 | 240 | Mpa |
| Tensile strain | Break,23°C | ISO 527-2 | 2.5 | % |
| Bending modulus | 23°C | ISO 178 | 15300 | Mpa |
| bending strength | 23°C | ISO 178 | 360 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 256 | °C |
| Melting temperature | ISO 3146 | 260 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 262 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.57 | g/cm³ | |
| Shrinkage rate | TD | ISO 294-4 | 1.0 | % |
| MD | ISO 294-4 | 0.40 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 4.0 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 1.2 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.