Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.34 g/cm³ |
Shrinkage rate | | ISO 294-4 | 1.0 % |
Shrinkage rate | | ISO 294-4 | 0.40 % |
Water absorption rate | | ISO 62 | 1.8 % |
Water absorption rate | | ISO 62 | 6.0 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | HB |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ISO 527-2 | 180 MPa |
Tensile strain | | ISO 527-2 | 5.0 % |
Tensile modulus | | ISO 527-2 | 9400 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179/1eA | 13 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 220 °C |
Heat distortion temperature | | ISO 75-2/A | 210 °C |
Continuous use temperature | | IEC 60216 | 115 °C |
ball-indentation hardness | | IEC 60695-10-2 | 通过 |
ball-indentation hardness | | IEC 60695-10-2 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.