ASA TAIRILAC® WE810P FCFC TAIWAN
387
- Properties:High glossAging resistanceWeather resistance
- Usages:Household goods
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 220℃/10kg | ASTM D-1238(ISO 1133) | 8 | g/10min |
| Shrinkage rate | 3.2mm | ASTM D-995 | 0.5-0.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23℃ | ASTM D-638(ISO 527) | 400(39) | kg/cm2(MPa) |
| bending strength | 23℃ | ASTM D-790(ISO 178) | 660(65) | kg/cm2(MPa) |
| Bending modulus | 23℃ | ASTM D-790(ISO 178) | 21000(2060) | kg/cm2(MPa) |
| Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | 100 | R scale |
| IZOD impact strength | 23℃,1/8"bar | ASTM D-256(ISO R180) | 16(157) | kg.cm/cm(J/m) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 18.6kg/cm2(1/2"bar) | ASTM D-648(ISO 75/A) | 84 | °C |
| Combustibility | FILE NO.E162823,1.5mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.