| physical property | Test Condition | Test Method | Test Result |
|---|
| Saturation, 23 ℃ | | % | 3.5到5.0 |
| Balance, 23 ℃, 50% RH | | % | 1.2到1.5 |
| Shrinkage rate | | % | 0.10到0.31 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | MPa | 222.76到370.34 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | MPa | 144.83到292.41 |
| Tensile modulus | | MPa | 8206.9到28000.0 |
| Tensile strain | | % | 1.9到3.1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 11.143到19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | V/mil | 840 |
| Volume resistivity | | ohms·cm | 1.0E+12到1.0E+14 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| flow | | mm/mm/°C | 142.2E-5到203.2E-5 |
| melting temperature | | °C | 260 |
| Continuous use temperature | | °C | 110到220 |
| 8.0Mpa, Not annealed | | °C | 65到220 |
| 1.8MPa, Not annealed | | °C | 230到250 |
| horizontal | | mm/mm/°C | 68.6E-5到127.0E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.