PC 104R-111 SABIC INNOVATIVE NANSHA

Form：Granules

Typical Applications:

Food packagingNursing suppliesMedical supplies

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:

Food packaging | Nursing supplies | Medical supplies

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
Refractive index	Refractive index		ISO 489	1.586
transmissivity	2540μm	ASTM D1003	88.0	%
turbidity	2540μm	ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	65.0	J
Dart impact	Dart impact	23°C	ASTM D3029	169	J
Impact strength of cantilever beam gap		ASTM D1822	630	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
Burning wire flammability index	1.0mm	IEC 60695-2-12	850	°C
Extreme Oxygen Index		ISO 4589-2	25	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D638	62.0	Mpa
	tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	Break	ASTM D638	68.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	70.0	Mpa
elongation	Yield	ASTM D638	7.0	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
elongation	Break	ASTM D638	140	%
Tensile strain	Break	ISO 527-2/50	120	%
Bending modulus	50.0mmSpan	ASTM D790	2340	Mpa
Bending modulus	Bending modulus		ISO 178	2300	Mpa
bending strength		ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	97.0	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	10.0	mg
Taber abraser	Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	10.0	mg
Tensile modulus		ASTM D638	2310	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2350	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6E-05	cm/cm/°C
specific heat		ASTMC351	1250	J/kg/°C
thermal conductivity		ASTMC177	0.19	W/m/K
thermal conductivity	thermal conductivity		ISO 8302	0.20	W/m/K
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Str		UL 746	130	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan10	ISO 75-2/Ae	127	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan11	ISO 75-2/Af	124	°C
Vicat softening temperature		ASTM D152512	154	°C
	Vicat softening temperature	--	ISO 306/B50	144	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	145	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Ball Pressure Test	Ball Pressure Test	140°C13	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	137	°C
	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	138	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	132	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Specific volume		ASTM D792	0.830	cm³/g
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0	g/10min
Melt Volume Flow Rate (MVR)	220°C/5.0kg	ISO 1133	4.00	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.00	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	24hr	ASTM D570	0.15	%
	Water absorption rate	Saturation,23°C	ISO 62	0.35	%
		Water absorption rate	Equilibrium,23°C	ASTM D570	0.35	%
			Water absorption rate	Equilibrium,100°C	ASTM D570	0.58	%
			Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	>1.0E+17	ohms·cm
Dielectric strength	3.20mm,inAir	ASTM D149	15	KV/mm
Dissipation factor	50Hz	IEC 60250	1E-03
	Dissipation factor	60Hz	IEC 60250	1E-03
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.010
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 1
High voltage arc tracing rate	HVTR	UL 746	PLC 2
Hot wire ignition	HWI	UL 746	PLC 2
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	KV/mm
Dielectric constant	50Hz	ASTM D150	3.17
	Dielectric constant	60Hz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	1MHz	ASTM D150	2.96
Relative permittivity	50Hz	IEC 60250	2.70
	Relative permittivity	60Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.70
Dissipation factor	50Hz	ASTM D150	9E-04
	Dissipation factor	60Hz	ASTM D150	9E-04
	Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.010
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	118
Ball Pressure Test	H358/30	ISO 2039-1	95.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.