PPSU RADEL® R-5900
496
- Properties:Resistance to stress cracThermal stability
- Usages:household electrical appliancesMedical devicesAerospace Applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 耐热性 耐化学性良好 阻燃 高韧性 | |||
| purpose | 电器用具 消费品应用领域 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 Mpa | |
| ASTM D638/ISO 527 | 2340 kg/cm²(MPa)[Lb/in²] | ||
| tensile strength | ASTM D638/ISO 527 | 70.3 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2340 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 100 kg/cm²(MPa)[Lb/in²] |
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| bending strength | ASTM D790 | 100 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 694 J/m | |
| Glass Transition Temperature | ASTM E1356 | 220 °C | |
| Linear expansion coefficient | ASTM D696 | 0.000056 cm/cm/℃ | |
| melt mass-flow rate | ASTM D1238 | 30 g/10min | |
| Shrinkage rate | ASTM D955 | 0.7 % | |
| Water absorption rate | ASTM D570 | 0.37 % | |
| tensile strength | ASTM D638 | 70.3 Mpa | |
| elongation | ASTM D638 | 7.2 % | |
| ASTM D638 | 60-120 % | ||
| Flexural modulus | ASTM D790 | 2410 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.29 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 207 °C | |
| Combustibility (rate) | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.