PBT LONGLITE® 1200
15
- Properties:High mobilityGood forming performanceExcellent surface finishFlow performanceGood formabilityGood surface gloss
- Usages:Switch panelMonitor
- Certificates:UL
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Fiber Content | Ash | 0 % | |
| Shrinkage rate | ASTM D-955 | 0.8-2.0 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.06 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D-790 | 750-850 kg/cm | |
| tensile strength | ASTM D-638 | 500-600 kg/cm | |
| Flexural modulus | ASTM D-790 | 22000 kg/cm | |
| Rockwell hardness | ASTM D-785 | 85-90 M-scale | |
| elongation at break | ASTM D-638 | 50-90 % | |
| Impact strength of cantilever beam gap | ASTM D-256 | 4.5-5.5 kg.cm/cm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Induced positive connection | ASTM D-150 | 0.001 | |
| Volume resistivity | ASTM D-257 | >10 Ω.cm | |
| Surface Resistivity | ASTM D-257 | >10 Ω | |
| dielectric strength | ASTM D-149 | 20 KV/mm | |
| arc resistance | ASTM D-495 | 120 sec | |
| dielectric constant | ASTM D-150 | 3.3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | DSC | 225 °C | |
| flame resistance | UL 94 | HB | |
| Heat distortion temperature | ASTM D-648 | 155 °C | |
| ASTM D-648 | 60 °C | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.