Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.20to0.40 % |
| Water absorption rate | | ASTM D570 | 0.25 % |
| Apparent density | | ASTM D1895 | 0.75 g/cm³ |
| density | | ASTM D792 | 1.91 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 75.0 MPa |
| Flexural modulus | | ASTM D790 | 11700 MPa |
| bending strength | | ASTM D790 | 124 MPa |
| compressive strength | | ASTM D695 | 150 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 32 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 14 kV/mm |
| dielectric constant | | ASTM D150 | 3.50 |
| Dissipation Factor | | ASTM D150 | 0.014 |
| arc resistance | | ASTM D495 | 130 sec |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648A | >280 °C |
| Heat distortion temperature | | ASTM D648A | >280 °C |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare