Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | cm³/10min | 0.05to0.07 |
| balance | | % | 0.055-0.21 |
| lateral flow | | mm/mm | 188.0E-3-208.3E-3 |
| flow | | mm/mm | 86.4E-3-0.330 |
| saturation | | % | 0.30-0.40 |
| Viscosity value | | ml/g | 80.0-95.0 |
| Apparent density | | g/cm³ | 0.70-0.80 |
| melt mass-flow rate | | g/10min | 17to22 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 110to120 |
| ball-indentation hardness | | | 110.34to251.72 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | °C | 648to960 |
| Limiting Oxygen Index | | % | 21 |
| burning rate | | mm/min | 0.0to99.06 |
| Hot filament ignition temperature | | °C | 643to960 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | % | 1.7-3.9 |
| yield | | % | 1.0-4.5 |
| fracture | | | 97.24to160.0 Mpa |
| yield | | | 163.45to172.41 Mpa |
| yield | | | 87.59to175.17 Mpa |
| yield | | % | 1.0-3.0 |
| fracture | | | 50.0to140.69 Mpa |
| yield | | | 89.66to140.69 Mpa |
| fracture | | % | 1.5-3.2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 5.572to15.323 |
| Charpy Notched Impact Strength | | kJ/m² | 1.067to2.229 |
| Dart impact | | N.m | 469.91to626.55 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1.0E+14-1.1E+15 |
| Volume resistivity | | ohms·cm | 1.0E+12-1.0E+16 |
| relative permittivity | | | 3.76 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 2 |
| Dissipation Factor | | | 8.0E-4-0.017 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| horizontal | | mm/mm/°C | 83.8E-5-152.4E-5 |
| RTI Imp | | °C | 75to125 |
| flow | | mm/mm/°C | 27.9E-5-50.8E-5 |
| flow | | mm/mm/°C | 30.5E-5-50.8E-5 |
| thermal conductivity | | W/m2k | 0.30to0.33 |
| horizontal | | mm/mm/°C | 76.2E-5-101.6E-5 |
| RTI | | °C | 75to140 |
| RTI Elec | | °C | 75to140 |
| melting temperature | | °C | 237to240 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare