Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 5.0 g/10 min |
| melt mass-flow rate | | ASTM D1238 | 14 g/10 min |
| melt mass-flow rate | | ASTM D1238 | 24 g/10 min |
| Shrinkage rate | | 内部方法 | 0.50 - 0.70 % |
| Shrinkage rate | | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | | ASTM D570 | 0.25 % |
| Outdoor applicability | | UL 746C | f2 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 94 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2500 Mpa |
| tensile strength | | ASTM D638 | 62.0 Mpa |
| tensile strength | | ISO 527-2/50 | 57.0 Mpa |
| tensile strength | | ISO 527-2/50 | 50.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 4.5 % |
| Tensile strain | | ASTM D638 | 25 % |
| Tensile strain | | ISO 527-2/50 | 130 % |
| Flexural modulus | | ASTM D790 | 2510 Mpa |
| Flexural modulus | | ISO 178 | 2500 Mpa |
| bending strength | | ISO 178 | 75.0 Mpa |
| bending strength | | ASTM D790 | 88.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 30.0 J |
| Dart impact | | ASTM D3763 | 47.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 95 to 105 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.040 % |
| Suggested injection volume | | | 40 to 80 % |
| Temperature at the rear of the barrel | | | 240 to 255 °C |
| Temperature in the middle of the barrel | | | 245 to 260 °C |
| Temperature at the front of the material cylinder | | | 250 to 265 °C |
| Spray nozzle temperature | | | 245 to 265 °C |
| Processing (melt) temperature | | | 260 to 275 °C |
| Temperature | | | 55 to 70 °C |
| Back pressure | | | 0.300 to 1.00 Mpa |
| screw speed | | | 30 to 80 rpm |
| Exhaust hole depth | | | 0.038 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 115 °C |
| Heat distortion temperature | | ISO 75-2/Bf | 116 °C |
| Heat distortion temperature | | ASTM D648 | 104 °C |
| Heat distortion temperature | | ISO 75-2/Af | 98.0 °C |
| vicat | | ISO 306/B50 | 113 °C |
| Linear coefficient of thermal expansion | | ASTM E831 | 7.2E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 7.2E-5 cm/cm/°C |
| thermal conductivity | | ASTM C177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.