SPS XAREC™ S135 IDEMITSU JAPAN

112

Properties:
Glass fiber reinforced
High temperature resistan
Usages:
Electrical applications
Household daily necessiti
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	内部方法	0.50to0.80	%
Shrinkage rate	Shrinkage rate	MD	内部方法	0.10to0.40	%
Water absorption rate	平衡,23°C,50%RH	ISO62	0.010	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	9700	Mpa
tensile strength	断裂	ISO527-2	125	Mpa
elongation	断裂	ISO527-2	2.0	%
Bending modulus		ISO178	9800	Mpa
bending strength		ISO178	200	Mpa
Impact strength of simply supported beam without notch	23°C	ISO179	40	kJ/m²
Cantilever beam without notch impact strength	23°C	ISO180	32	kJ/m²

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	270	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	250	°C
Linear coefficient of thermal expansion	MD：-30到30°C	TMA	1.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	TMA	4.3E-05	cm/cm/°C
RTIElec		UL746	50.0	°C
RTI Imp		UL746	50.0	°C
RTIStr		UL746	50.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	>1.0E+16	ohms·cm
Dielectric strength		ASTMD149	45	KV/mm
Dielectric constant	1MHz	IEC60250	2.90
Dissipation factor	1MHz	IEC60250	<1.0E-3
Compared to the anti leakage trace index	CTI)3	IEC60112	PLC1

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8到3.0mm,全部	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.