Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.55 g/cm³ |
| Water absorption rate | | ISO 62 | 0.13 % |
| Shrinkage rate | | ISO 294-4 | 0.4-0.8 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.09 % |
| density | | ASTM D-792 | 1.55 g/cm3 |
| Shrinkage rate | | ASTM D-955 | 0.4-0.8 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 135 MPa |
| elongation | Break | ISO 527 | 2.5 % |
| bending strength | | ISO 178 | 220 MPa |
| Flexural modulus | | ISO 178 | 10500 MPa |
| Notch impact strength | | ISO 179(1eA) | 10 KJ/m² |
| tensile strength | | ASTM D-638 | 120 MPa |
| elongation | | ASTM D-638 | 4.2 % |
| bending strength | | ASTM D-790 | 190 MPa |
| Charpy impact strength | | ISO 179 | 40 KJ/M2 |
| Charpy impact strength | Notched | ISO 179 | 10 KJ/M2 |
| Flexural modulus | | ASTM D-790 | 8000 MPa |
| Impact strength of cantilever beam gap | | ASTM D-256 | 80 J/m |
| Rockwell hardness | | ASTM D-785 | 88 M scale |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | UL 94 | HB |
| Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | UL94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 3 |
| | ASTM D-257 | 1014 Ω.cm |
| Loss factor | | ASTM D-150 | 2.5×10-2 106Hz |
| dielectric strength | | ASTM D-149 | 21 MV/m |
| dielectric constant | | ASTM D-150 | 3.0 106HZ |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75f | 210 ℃ |
| | ASTM D-696 | 2.5 10-5℃mm/mm/℃ |
| | ASTM D-648 | 208 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.