Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ASTM D3835 | 545 Pa·s |
| density | | ASTM D471 | 1.19 g/cm³ |
| density | | ISO 2781 | 1.19 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| DurometerHardness | | ASTM D2240 | 62 |
| Shore hardness | | ISO 868 | 62 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Taber abraser | | ASTM D1044 | 7.00 mg |
| Torsion Module | | ASTM D1043 | 7.50 MPa |
| Torsion Module | | ASTM D1043 | 1.90 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Stretch permanent deformation | | ASTM D412 | 8 % |
| tensile strength | | ASTM D412 | 3.90 MPa |
| tensile strength | | ASTM D573 | 3.90 MPa |
| tensile strength | | ISO 37 | 3.90 MPa |
| tensile strength | | ISO 188 | 3.90 MPa |
| tensile strength | | ASTM D412 | 9.60 MPa |
| Clash Mountain Module | | ASTM D1043 | 68.9 MPa |
| tensile strength | | ASTM D573 | 10.6 MPa |
| tensile strength | | ISO 37 | 9.60 MPa |
| tensile strength | | ISO 188 | 10.6 MPa |
| elongation | | ASTM D573 | 330 % |
| elongation | | ASTM D412 | 300 % |
| elongation | | ISO 37 | 300 % |
| elongation | | ISO 188 | 330 % |
| tear strength | | ASTM D624 | 26.3 kN/m |
| compression set | | ASTM D395B | 15 % |
| compression set | | ASTM D395B | 55 % |
| compression set | | ISO 815 | 15 % |
| compression set | | ISO 815 | 55 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Hardness change rate in the air | | ASTM D573 | 5.0 |
| volume change | | ISO 1817 | 30 % |
| volume change | | ISO 1817 | -10 % |
| volume change | | ISO 1817 | 27 % |
| volume change | | ISO 1817 | 12 % |
| Shore hardness | | ISO 188 | 5.0 |
| volume change | | ASTM D471 | 30 % |
| volume change | | ASTM D471 | -10 % |
| volume change | | ASTM D471 | 27 % |
| volume change | | ASTM D471 | 12 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -51.0 °C |
| brittle temperature | | ISO 812 | -51.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.