PC/ABS C2950HF-111 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh mobilityHigh impact resistanceHigh temperature resistanheat-resisting

Typical Applications:

Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Household appliances \| Household appliances \| Automotive sector
Properties:	Flame retardant \| High mobility \| High impact resistance \| High temperature resistan \| heat-resisting

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	54.2	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.76mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	2.5mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.4mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	30	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,100mmSpan	ASTM D790	96.5	Mpa
tensile strength	Yield	ASTM D638	64.1	Mpa
elongation	Yield	ASTM D638	5.0	%
elongation	elongation	Break	ASTM D638	40	%
Bending modulus	100mmSpan	ASTM D790	2590	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	102	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	87.8	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	93.3	°C
Vicat softening temperature		ASTM D15254	113	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	7.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	7.2E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.20	W/m/K
RTI Elec		UL 746	85.0	°C
RTI Imp		UL 746	85.0	°C
RTI Str		UL 746	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260°C/2.16kg	ASTM D1238	22	g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60	%
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.40-0.60	%
Water absorption rate	24hr	ASTM D570	0.10	%
Water absorption rate	Water absorption rate	Equilibrium,23°C	ASTM D570	0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	50Hz	ASTM D150	5.2E-03
	Dissipation factor	60Hz	ASTM D150	5.2E-03
	Dissipation factor	Dissipation factor	1MHz	ASTM D150	7.1E-03
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 2
Surface resistivity		ASTM D257	>1.0E+16	ohms
Volume resistivity		ASTM D257	1.6E+17	ohms·cm
Dielectric strength	3.20mm,inOil	ASTM D149	24	KV/mm
Dielectric constant	50Hz	ASTM D150	2.80
	Dielectric constant	60Hz	ASTM D150	2.80
	Dielectric constant	Dielectric constant	1MHz	ASTM D150	2.70
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.