PC+ABS T65 PG

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ISO2577	0.50to0.70 %
Shrinkage rate	Shrinkage rate		ISO2577	0.50to0.70 %
Water absorption rate		ISO62	0.70 %
Water absorption rate	Water absorption rate		ISO62	0.20 %
MeltViscosity		ISO11443-A	200 Pa·s
density		ISO1183	1.13 g/cm³
Melt volume flow rate		ISO1133	18.0 cm³/10min

flammability	Test Condition	Test Method	Test Result
FlameRating		UL94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2/1	2400 MPa
Tensile stress		ISO527-2/50	54.0 MPa
Tensile stress	Tensile stress		ISO527-2/50	47.0 MPa
Tensile strain		ISO527-2/50	4.4 %
Tensile strain	Tensile strain		ISO527-2/50	>50 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO180/A	35 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/A	45 kJ/m²
		ISO180	NoBreak
			ISO180	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
		IEC60250	3.00
Dissipation Factor		IEC60250	3E-03
Dissipation Factor	Dissipation Factor		IEC60250	8.5E-03
CTI		IEC60112	250 V
Surface Resistivity		IEC60093	1E+16 ohms
Volume resistivity		IEC60093	1E+16 ohms·cm
dielectric strength		IEC60243-1	35 kV/mm
		IEC60250	3.10

Thermal performance	Test Condition	Test Method	Test Result
		ISO75-2/B	122 °C
			ISO75-2/A	102 °C
vicat		ISO306/B50	118 °C
vicat	vicat		ISO306/B120	120 °C
		ISO11359-2	8E-05 cm/cm/°C
			ISO11359-2	8.5E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.