Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 2.0到3.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.75到0.90 % |
| Water absorption rate | | ASTMD570 | 0.16到0.19 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 85到127 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTMD638 | 78到120 % |
| Flexural modulus | | ASTMD790 | 2030到2330 MPa |
| bending strength | | ASTMD790 | 95.1到97.2 MPa |
| Tensile stress | | ISO527-2 | 65.0到65.1 MPa |
| Tensile stress | | ASTMD638 | 71.7到77.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 370到640 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 3200 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 2.6E+16到2.6E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| dielectric constant | | ASTMD150 | 3.00到3.27 |
| Dissipation Factor | | ASTMD150 | 1.2E-3到0.024 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 143到149 °C |
| vicat | | ISO306 | 154到167 °C |
| | ASTME831 | 6.0E-5到9.2E-5 cm/cm/°C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| RTI Elec | | UL746 | 125到130 °C |
| RTI Imp | | UL746 | 125到130 °C |
| RTI | | UL746 | 125到130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.