PETG 0601 EASTMAN USA

Form：Granules | Grade：Injection grade

Properties:

High transparencyHigh toughness

Typical Applications:

sporting goodschip

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	sporting goods \| chip
Properties:	High transparency \| High toughness

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	45°	ASTM D2457	108
transmissivity	常规	ASTM D1003	89.0	%
transmissivity	transmissivity	Total	ASTM D1003	91.0	%
transparency		ASTM D1746	85.0
turbidity		ASTM D1003	0.80	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,3.20mm,能量to力量峰值8,9	ISO 6603-2	44.0	J
	Dart impact	23°C,2.50mm,能量to力量峰值8,9	ISO 6603-2	40.0	J
		Dart impact	-40°C,3.20mm,能量to力量峰值8,9	ISO 6603-2	36.0	J
			Dart impact	-40°C,2.50mm,能量to力量峰值8,9	ISO 6603-2	35.0	J
				Dart impact	23°C,3.20mm,EnergyatPeakLoad	ASTM D3763	33.0	J
					Dart impact	23°C,2.50mm,EnergyatPeakLoad	ASTM D3763	28.0	J
						Dart impact	-40°C,3.20mm,EnergyatPeakLoad	ASTM D3763	50.0	J
						Dart impact	Dart impact	-40°C,2.50mm,EnergyatPeakLoad	ASTM D3763	41.0	J
Suspended wall beam without notch impact strength	23°C7	ISO 180/1U	无断裂
	Suspended wall beam without notch impact strength	-20°C7	ISO 180/1U	无断裂
		Suspended wall beam without notch impact strength	-30°C7	ISO 180/1U	无断裂
			Suspended wall beam without notch impact strength	-40°C7	ISO 180/1U	无断裂
				Suspended wall beam without notch impact strength	23°C,3.20mm	ASTM D4812	无断裂
					Suspended wall beam without notch impact strength	-20°C,3.20mm	ASTM D4812	无断裂
						Suspended wall beam without notch impact strength	-30°C,3.20mm	ASTM D4812	无断裂
						Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-40°C,3.20mm	ASTM D4812	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ASTMD638	2100	Mpa
tensile strength	Yield,23°C	ASTMD638	50.0	Mpa
tensile strength	tensile strength	Break,23°C	ASTMD638	28.0	Mpa
elongation	Break,23°C	ASTM D638	130	%
elongation	elongation	Break,23°C	ISO 527-2	100	%
Bending modulus	23°C	ASTM D790	2100	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2000	Mpa
bending strength	23°C	ISO 178	68.0	Mpa
bending strength	bending strength	Yield,23°C	ASTM D790	70.0	Mpa
tear strength	M.D.:23°C	-	93	N
tear strength	tear strength	T.D.:23°C	-	93	N
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525	85.0	°C
Glass transition temperature		DSC	80.0	°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	64.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	70.0	°C
Linear coefficient of thermal expansion	MD：-30to40°C	ASTM D696	5.1E-05	cm/cm/°C
specific heat	60°C	DSC	1300	J/kg/°C
	specific heat	100°C	DSC	1760	J/kg/°C
		specific heat	150°C	DSC	1880	J/kg/°C
			specific heat	200°C	DSC	1970	J/kg/°C
			specific heat	specific heat	250°C	DSC	2050	J/kg/°C
thermal conductivity	23°C	ASTMC177	0.21	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Intrinsic viscosity	Pellets:23°C	Internal Method	0.75
Intrinsic viscosity	Intrinsic viscosity	Film:23°C	Internal Method	0.70
Water absorption rate	23°C,24hr	ASTMD570	0.13	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	23°C	ASTM D149	16	KV/mm
Dielectric constant	23°C,1kHz	ASTM D150	2.60
Dielectric constant	Dielectric constant	23°C,1MHz	ASTM D150	2.40
Dissipation factor	23°C,1kHz	ASTM D150	5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	ASTM D150	0.020
Arc resistance		ASTM D495	158	sec
Surface resistivity		ASTM D257	1E+16	ohms
Volume resistivity	23°C	ASTM D257	1E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	109
Rockwell hardness	Rockwell hardness	R-Scale,23°C	ASTM D785	106
film	Test Condition	Test Method	Test Result	Test Unit
Tear resistance of pants type	TD	ISO 6383-1	36.0	N/mm
Oxygen permeability	23°C	ASTM D3985	10	cm³·mm/m²/atm/24hr
Water vapor permeability	38°C,100%RH	ASTMF1249	7.0	g/m²/24hr
Carbon dioxide transmittance	23°C	ASTM D1434	49	cm³·mm/m²/atm/24hr
tear strength	M.D.:23°C	ASTM D1938	36	kN/m
tear strength	tear strength	T.D.:23°C	ASTM D1938	36	kN/m
tensile strength	TD:Break	ASTM D882	55.0	Mpa
elongation	MD:Yield	ASTM D882	4.0	%
	elongation	TD:Yield	ASTM D882	4.0	%
		elongation	MD:Break	ASTM D882	400	%
		elongation	elongation	TD:Break	ASTM D882	400	%
Dart impact	-18°C	ASTM D1709A	500	g
Dart impact	Dart impact	23°C	ASTM D1709A	400	g
Elmendorf tear strength	MD	ASTM D1922	1400	g
Elmendorf tear strength	Elmendorf tear strength	TD	ASTM D1922	1700	g
Tear resistance of pants type	MD	ISO 6383-1	36.0	N/mm
film thickness			250	µm
Secant modulus	MD	ASTM D882	1900	Mpa
Secant modulus	Secant modulus	TD	ASTM D882	1900	Mpa
tensile strength	MD:Yield	ASTM D882	52.0	Mpa
	tensile strength	TD:Yield	ASTM D882	52.0	Mpa
	tensile strength	tensile strength	MD:Break	ASTM D882	59.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.