| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.09 g/cm³ |
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| melt mass-flow rate | | ISO1133 | 67 g/10min |
| melt mass-flow rate | | ISO1133 | 1.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 73 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 25.8 MPa |
| Tensile stress | Break | ISO527-2 | 20.4 MPa |
| Tensile strain | Break | ISO527-2 | 25 % |
| Flexural modulus | | ISO178 | 2020 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | 5E+03 ohms |
| Surface Resistivity | | 内部方法 | 1E+03 ohms |
| Volume resistivity | | 内部方法 | 1E+02 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 67.0 °C |
| vicat | | ISO306/A | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.