PA6 B3S BASF MALAYSIA

Form：Granules | Grade：Injection grade

Properties:

crystallizationHigh mobilityFast forming cycleOil resistant

Typical Applications:

Thin walled componentspartsShellpartsShellThin walled components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Thin walled components \| parts \| Shell \| parts \| Shell \| Thin walled components
Properties:	crystallization \| High mobility \| Fast forming cycle \| Oil resistant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	3.0	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	4.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180	3.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	250	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	200	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	3000	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	10	%
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
tensile strength	Yield,23°C	ISO 527-2	90.0	Mpa
Tensile modulus	23°C	ISO 527-2	3400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 3146	220	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.13	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	3.0	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	9.5	%
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	175	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112		V
Dissipation factor	1MHz	IEC 60250	0.030
Dielectric constant	1MHz	IEC 60250	3.30
Volume resistivity		IEC 60093	1E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	160	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.