EAA 30707 DUPONT USA

Form：Granules | Grade：Blow molding grade

Properties:

Heat sealing performance

Typical Applications:

sealantPharmaceutical packagingMedical packaging

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	sealant \| Pharmaceutical packaging \| Medical packaging
Properties:	Heat sealing performance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity		ASTM D-1003	3	%
other	Test Condition	Test Method	Test Result	Test Unit
characteristic			良好的热密封.低温热封闭
Color			透明
purpose			良好的热密封.低温热封闭
machinability	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			60	°C
Melt Temperature			150	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Secant modulus	MD，1% Strain	ASTM D-882	170	MPa
Secant modulus	Secant modulus	TD，1% Strain	ASTM D-882	175	MPa
Elongation at Break	TD	ASTM D-882	560	%
Elongation at Break	Elongation at Break		ASTM D638/ISO 527	500	%
Tensile modulus		ASTM D638/ISO 527	100	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	28.5	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	80
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature	DSC		102	℃
Vicat softening temperature		ASTM D-1525	84	℃
Vicat softening temperature	Vicat softening temperature		ISO 306	84	℃
FreezingPoint	--	ASTM D3418	85	°C
Vicat softening temperature		ASTM D1525	84.0	°C
Vicat softening temperature	Vicat softening temperature		ISO 306	84.0	°C
Melting temperature		ASTM D3418	102	°C
Melting temperature	Melting temperature		ISO 3146	102	°C
FreezingPoint	--	ISO 3146	85	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	7.0	g/10min
melt mass-flow rate	melt mass-flow rate	190°C/2.16kg	ISO 1133	7.0	g/10min
AcrylicAcidContent			7.0	wt%
density		ASTM D792/ISO 1183	0.93
Water absorption rate		ASTM D570/ISO 62	0.002	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.